vol.63Simultaneous multi-element electrothermal atomic absorption determination using a low resolution CCD spectrometer and continuum light source: The concept and methodologyA DFT and NBO analysis of the bonding in titanocenyl complexes containing a five-membered L,L'-cyclic ligand: L,L' = O,O'; S,S' or Se,Se' índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados



Links relacionados

  • En proceso de indezaciónCitado por Google
  • En proceso de indezaciónSimilares en Google


South African Journal of Chemistry

versión On-line ISSN 1996-840X
versión impresa ISSN 0379-4350


CAO, Yong et al. Synthesis of nitrogen-doped carbon nanotubes with layered double hydroxides containing iron, cobalt or nickel as catalyst precursors. S.Afr.j.chem. (Online) [online]. 2010, vol.63, pp.58-61. ISSN 1996-840X.

Nitrogen-doped carbon nanotubes (CNx) were synthesized by the catalytic chemical vapour deposition of ethylenediamine with layered double hydroxides (LDHs) containing iron, cobalt or nickel as catalyst precursors at 650 °C. The catalytically active metal particles were obtained by calcination of LDHs followed by reduction. X-ray diffraction was used to characterize the structures of the precursors and their calcined products. Transmission electron microscopy, X-ray photoelectron spectroscopy and Raman spectroscopy were used to characterize the grown CNx. The results show that the CNx grown with Mg2 Fe-LDH as catalyst precursor have abamboo-like morphology and large diameter, while hollow tubes are obtained with CoMgAl- and NiMgAl-LDH as catalyst precursors. The CNx grown with CoMgAl-LDH have the highest N-doped content and the CNx grown with NiMgAl-LDH have the highest degree of graphitization among these three products.

Palabras clave : N-doped carbon nanotubes; layered double hydroxides; chemical vapour deposition.