SciELO - Scientific Electronic Library Online

 
vol.114 número4The recovery of manganese products from ferromanganese slag using a hydrometallurgical routeComparing the extent of the dissolution of copper-cobalt ores from the DRC Region índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados

Articulo

Indicadores

Links relacionados

  • En proceso de indezaciónCitado por Google
  • En proceso de indezaciónSimilares en Google

Compartir


Journal of the Southern African Institute of Mining and Metallurgy

versión On-line ISSN 2411-9717
versión impresa ISSN 0038-223X

Resumen

LANGE, M.; GARBERS-CRAIG, A.M.  y  CROMARTY, R.. Wear of magnesia-chrome refractory bricks as a function of matte temperature. J. S. Afr. Inst. Min. Metall. [online]. 2014, vol.114, n.4, pp.341-346. ISSN 2411-9717.

The postulation that primary platinum group metal (PGM) matte will chemically react with magnesia-chrome bricks when temperatures exceed 1500°C was tested. Magnesia-chrome brick samples were heated in contact with matte at 1300°C to 1750°C for 30 minutes, after which the refractory samples were analysed using reflected light microscopy and scanning electron microscopy. The samples were all completely penetrated by matte. As the temperature increased the matte also penetrated the fused aggregate grains and disintegrated them. The chromium concentration of the matte inside the refractory samples was found to be slightly higher than that of the bulk matte. At temperatures of 1500°C and higher, MgO, FeO, and magnesium-rich silicate crystals could be identified in the matte directly adjacent to the refractorymatte interface. Phase relations clearly indicated that chemical reactions take place between primary PGM matte and the magnesia-chrome refractory material at temperatures above 1500°C, but that these reactions are more complex than expected from FactSAGE® calculations.

Palabras clave : refractory; magnesia-chrome bricks; penetration; fused grains.

        · texto en Inglés

 