vol.113 número2Effect of cold reduction and annealing temperature on texture evolution of AISI 441 ferritic stainless steelFriction Hydro Pillar Process as an alternative repair technology for creep evaluation sites on thick-walled 10CrMo910 creep-resistant steel structures índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Journal of the Southern African Institute of Mining and Metallurgy

versão On-line ISSN 2411-9717

Resumo

MULAUDZI, F.M.L. et al. A study of metal dusting corrosion on Fe- and Ni-based alloys. J. S. Afr. Inst. Min. Metall. [online]. 2013, vol.113, n.2, pp. 121-128. ISSN 2411-9717.

Behaviour studies of metal dusting processes and associated filamentous carbon formation were undertaken on Alloys 600, 601, and 800 using a simulated metal dusting environment of 25CO-70H2-5H2O (vol.%) at 650°C. These samples were studied visually and by optical microscopy, scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM-EDX), transmission electron microscopy with energy-dispersive X-ray spectroscopy (TEM-EDX) and X-ray diffraction (XRD). Visual examination and SEM surface observation showed that Alloy 800 suffered metal dusting attack at an early exposure reaction period. The coke deposit amounts increased significantly with reaction time from 168 hours to 336 hours in Alloys 600, 601, and 800. Alloy 800 showed pitting after 168 hours' exposure, and the degree of pitting increased after 336 hours. XRD showed all these alloys had a common austenitic phase, with Alloy 800 also having ferritic metal particles. Alloy 800 after 168 hours' exposure had a complex phase mixture on the surface, consisting of ferritic Fe and austenitic FeNi phases. For coke deposit, there were also Fe3O4, Fe3C and graphitic carbon. The existence of Fe, Ni, and Cr metal particles, and also graphitic carbon in coke deposits, was confirmed by EDX analyses.

Palavras-chave : metal dusting; Alloy 600; Alloy 601; Alloy 800; SEM; TEM; XRD.