SciELO - Scientific Electronic Library Online

 
vol.113 número2Effect of dual phase microstructure on the toughness of a Cr-Mo low-alloy plate steelA study of metal dusting corrosion on Fe- and Ni-based alloys índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Journal of the Southern African Institute of Mining and Metallurgy

versão On-line ISSN 2411-9717
versão impressa ISSN 0038-223X

Resumo

MARUMA, M.G.; SIYASIYA, C.W.  e  STUMPF, W.E.. Effect of cold reduction and annealing temperature on texture evolution of AISI 441 ferritic stainless steel. J. S. Afr. Inst. Min. Metall. [online]. 2013, vol.113, n.2, pp.115-120. ISSN 2411-9717.

The effect of the amount of cold reduction and annealing temperature on the evolution of the texture of AISI 441 steel is reported. The steel was cold rolled by 62%, 78%, and 82%, followed by isothermal annealing of each sample at 900°C, 950°C, and 1025°C for 3 minutes. The crystallographic texture was determined by Phillips X'Pert PRO MPD texture diffractrometer. Microstructures were characterized using optical microscopy and scanning electron microscopy (SEM). The results show that sample that received 78% cold reduction and annealing at 1025°C presented the highest Rm-value and lowest ΔR-value, which would enhance its deep-drawing capability. In addition, this sample showed the highest intensity of shifted γ-fibre, notably {554}<225> and {334}<483>. It can therefore be concluded that the γ-fibre, which favours deep drawing, is optimal after 78% cold reduction and annealing at 1025°C.

Palavras-chave : ferritic stainless steel; texture; XRD.