SciELO - Scientific Electronic Library Online

 
vol.113 número2Evaluation of oxine-type ligand coordination to zirconium (IV)Effect of cold reduction and annealing temperature on texture evolution of AISI 441 ferritic stainless steel índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Journal of the Southern African Institute of Mining and Metallurgy

versão On-line ISSN 2411-9717
versão impressa ISSN 0038-223X

Resumo

LEACH, L.J.; SIYASIYA, C.W.  e  STUMPF, W.E.. Effect of dual phase microstructure on the toughness of a Cr-Mo low-alloy plate steel. J. S. Afr. Inst. Min. Metall. [online]. 2013, vol.113, n.2, pp.109-113. ISSN 2411-9717.

Quench and tempered Cr-Mo plate steel was found not to contain a fully martensitic structure as a result of either slow slack quenching or insufficient hardenability at the cooling rates used. The resulting microstructure contains bainite in combination with martensite. It is necessary to examine the implications of bainite for the toughness of the final product. Loss of toughness arises primarily from the inter-lath carbides that typically form in upper bainite. An investigation into the effect of upper bainite in a martensitic matrix of a steel grade containing 0.17% C, 0.1% Cr, 0.54% Mo, and 20 ppm B indicated lower toughness than in a fully martensitic structure.

Palavras-chave : upper bainite; toughness; instrumented impact.