JANKOVIC, A.; DUNDAR, H.  e  MEHTA, R.. Relationships between comminution energy and product size for a magnetite ore. J. S. Afr. Inst. Min. Metall. [online]. 2010, vol.110, n.3, pp. 141-146. ISSN 2411-9717.

An extensive laboratory grinding study was carried out on a magnetite ore in order to assess the grinding behaviour of magnetic concentrate and tail from low intensity magnetic separation (LIMS). The test work involved Bond ball mill testing, rod milling, low intensity magnetic separation (LIMS), and batch ball milling down to product sizes of around P80~25 microns. A total of 18 Bond tests and over 150 batch grinding tests and sieve sizing were carried out. Throughout the grinding tests, power draw was continuously monitored. The relationship between the grinding energy and product size was analysed using the conventional energy-size concepts. It was found that the Rittinger equation fits the experimental data well. However, Bond's equation does not fit the experimental data well, and therefore a modified Bond equation was developed. Differences in grinding properties between the magnetic and non-magnetic component were analysed and compared to the bulk ore. It was found that grinding properties differ significantly and therefore separate grinding test work may be required for each grinding step in the magnetite ore beneficiation flowsheet.

Palavras-chave : grinding; iron ores; particle size; modelling.